Product name

PA6/PA66 reinforced with (5%-55%)GF / (10%-50%)toughness /(V0,V1,V2)FR/ UV

Color

As required

Advantage

Competitive price,high quality,on-time delivery,free sample

Environment friendly

High Heat Resistance,High impact resistance

Without any impurity

Can be reinforced with the glass fiber/toughness/flame retardant/UV stabilizer

Packing

25kg/bag (also can be customized)

Item

Typical Characteristic

Testing Standard

KY-N6701

KY-N6702

 Density  

1.60g/cm3

1.55g/cm3

ASTM D-792

 Ggraphite content

10%

20%

---

  Melt Flow Rate      

6g/10min

4g/10min

ASTM D-1238

Molding Shrinkage

0.3-0.4%

0.5-0.7%

ASTM D-955

Water Absorption

0.40%

0.30%

ASTM D-570

Tensile Strength      

60MPa

75MPa

ASTM D-638

 Flexural Strength          

81MPa

70MPa

ASTM D-790

Elongation at break

11%

7%

ASTM D-638

 Flexural Modulus         

4500MPa

4000MPa

ASTM D-790

 Izod Notched Impact Strength

50J/m 

60J/m

ASTM D-256

Melting Point

245℃

260℃

ASTM D-648

  Heat Deflection Temperature

185℃

220℃

ASTM D-648

Flame Retardant

V1

V1

UL 94

 Surface Resistivity

10^11 Ohms/square

10^10 Ohms/square

IEC60093（dry）

Thermal conductivity

0.6W/mK

1.2±0.3W/mK

ASTM D-5470

Volume Resistivity

10^14Ω.cm

10^12Ω.cm

IEC60093(dry)

 Dielectric Strength

50kV/mm

20kV/mm

IEC 60243-1

 CTI  

450V

580V

IEC 60112

Use temperature

Processing temperature : 250 - 290 °C

Mould temperature      : 100 - 120 °C

Back pressure          : ca.10 - 15 bar

Injection speed        :  medium/high

Pre-drying             : necessary